Inorganic organic hybrid Pb-Sn mixed perovskites for photovoltaics

Rajapakshe Mudiyanselage, Indrachapa B. (2019) Inorganic organic hybrid Pb-Sn mixed perovskites for photovoltaics Doctoral thesis, University of Surrey.

Indrachapa Bandara R M _PhD Thesis Final.pdf - Version of Record
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (14MB) | Preview


Inorganic-organic hybrid metal halide perovskites have shown great promise in realising high performing photovoltaic devices with low fabrication cost. In this regard, Pb-Sn mixed perovskites are considered as highly suitable candidate for all perovskite tandem solar cells and single junction solar cells with narrow bandgaps. However, the maximum achievable performances of Pb-Sn mixed perovskite solar cells (PSCs) are not yet obtained due to the lack of understanding of the material system as well prevailing issues due to unintentional doping as a result of Sn oxidation. In this thesis, the optimisation of a triple cation Pb-Sn mixed perovskite with a formula Cs0.05(FA0.83MA0.17)0.95Pb0.5Sn0.5I3 was investigated. Firstly, the effect of the “anti-solvent” on Pb-Sn mixed perovskites (fabricated through the commonly used anti-solvent dripping method) was investigated and compared to a Pb-only triple cation perovskite analogue, in terms of its effect on the film morphology, crystallisation dynamics and molecular interactions in the films. Secondly, the need for careful selection of anti-solvents for Sn-incorporated PSCs, compared to their Pb-based counterparts is elaborated. This is investigated using Pb-Sn mixed perovskite devices of an inverted architecture, with a device stack of ITO/PEDOT:PSS/Perovskite/PC60BM/ZnO/BCP/Ag. The above studies, in combination with the film processing conditions used is identified to enable the removal of unwanted Sn4+ dopants, through engineering the anti-solvent method for Pb-Sn mixed perovskites. Optimisation of the anti-solvent engineering process enables an 80% enhancement in efficiency when toluene is used as the antisolvent, in comparison to the other anti-solvents tested in this work. The champion power conversion efficiency of 11.6% achieved through this is further improved to 12.04% following optimised anti-solvent wash and thermal treatment. This is attributed to the complete removal of Sn4+ dopants following the optimisation process. Following the optimisation of the Pb-Sn mixed perovskite film preparation, a surface post-treatment method is developed based on guanidinium bromide which enables the efficiency to be improved even further to 14.4%. The surface post-treatment especially allows device fill factors of 83%, the highest reported for Pb-Sn mixed PSCs reported so far, approaching the Shockley-Queisser limit for fill factors in Pb-Sn perovskites. This work highlights the importance of careful selection of anti-solvents and post treatments on Pb-Sn mixed perovskite absorber layers, in managing defects and reducing non-radiative recombination for high efficiency low bandgap perovskite materials, and also enables further improvements in device efficiency for all-perovskite tandem solar cells.

Item Type: Thesis (Doctoral)
Divisions : Theses
Authors :
Rajapakshe Mudiyanselage, Indrachapa B.0000-0003-4239-2535
Date : 30 September 2019
Funders : University of Surrey PhD scholarship
DOI : 10.15126/thesis.00853279
Contributors :
ContributionNameEmailORCID, S. Ravi
Depositing User : Indrachapa Bandara Rajapakshe Mudiyanselage
Date Deposited : 07 Feb 2020 14:44
Last Modified : 07 Feb 2020 14:44

Actions (login required)

View Item View Item


Downloads per month over past year

Information about this web site

© The University of Surrey, Guildford, Surrey, GU2 7XH, United Kingdom.
+44 (0)1483 300800