Grain and pore morphologies in polycrystals.

Rinous, Peter John. (1981) Grain and pore morphologies in polycrystals. Doctoral thesis, University of Surrey (United Kingdom)..

[img]
Preview
Text
10804406.pdf
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (5MB) | Preview

Abstract

Grain and pore morphologies are investigated in polycrystals which have an idealised microstructure. For such polycrystals pore behaviour and paths to grain growth are well defined due to the high degree of symmetry present. This is in contrast to. the intractable randomness generally observed in reality. Grain growth in non-porous structures is investigated in both two and three dimensions, Chapters 2 and 3 respectively. Two models in particular are considered. In the first growth is initiated by a single rogue grain either shrinking or growing in an otherwise uniform array of grains until an unstable configuration results. It is found that if the rogue grain shrinks the material can recrystallise into a uniform array of larger grains. If the rogue grain grows abnormal growth is expected to follow. In the second model growth in regular structures is considered. Such structures comprise n(n= 1,2,3) different types of grain which pack together in a regular way to fill space. Growth occurs because of instabilities arising from the different types of grain present and is assumed to occur in such a way that regularity, or homogeneity, throughout the material Is retained at all times. These models of grain growth developed here are entirely geometrical. Also in Chapter 2 we develop a model to investigate the effect of grain edge pore drag in' two-dimensional polycrystals. The expected qualitative behaviour is predicted. Chapter 4 is concerned with the stability and morphology of interlinked porosity in three-dimensional regular bimodal polycrystals. Here the material comprises two types of tetrakaidecahedra, large and small, enabling the effects of grain size variation on pore stability to be investigated. The results obtained here are interpreted with respect to the sintering of powder compacts and fission gas release which occurs during the irradiation of UO[2] nuclear fuel. It is found that during sintering interlinked porosity breaks down earlier than previously pre-dieted. It is also found that the fractional pore volume required to support an interconnected tunnel structure in UO2 during irradiation is almost insensitive to grain size variation. Both of these results are in good agreement with experimental observations. In Chapter 5 preliminary methods are developed to enable the results of Chapter 4, initially pertaining only to idealised materials, to be applied to materials with more realistic grain size distributions.

Item Type: Thesis (Doctoral)
Divisions : Theses
Authors :
NameEmailORCID
Rinous, Peter John.
Date : 1981
Contributors :
ContributionNameEmailORCID
http://www.loc.gov/loc.terms/relators/THS
Additional Information : Thesis (Ph.D.)--University of Surrey (United Kingdom), 1981.
Depositing User : EPrints Services
Date Deposited : 22 Jun 2018 14:25
Last Modified : 06 Nov 2018 16:53
URI: http://epubs.surrey.ac.uk/id/eprint/847945

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year


Information about this web site

© The University of Surrey, Guildford, Surrey, GU2 7XH, United Kingdom.
+44 (0)1483 300800