The effect of carbides on temper embrittlement of commercial 2.25Cr - 1Mo steel.

Muhammad, Azali bin. (1982) The effect of carbides on temper embrittlement of commercial 2.25Cr - 1Mo steel. Doctoral thesis, University of Surrey (United Kingdom)..

[img]
Preview
Text
10804294.pdf
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (16MB) | Preview

Abstract

Temper embrittlement has, been studied in samples tempered at different temperatures and for varying times to produce the same hardness (190VPN) and different hardness levels with different types of carbide. The specimens have been embrittled by isothermal ageing at 500°C for times up to 5,000 hrs. The embrittlement has been characterised by Charpy impact testing to determine the ductile-brittle transition temperature together with hardness testing. Types of carbides have been identified from energy dispersive X-ray (EDAX) spectra using carbon extraction replicas and their relative presence determined from transmission electron micrographs. Auger electron spectroscopy (AES) analysis has been used to monitor the change in grain boundary composition after ageing treatment. This study shows that types of carbides and their relative presence in the steel have a marked effect on temper embrittlement. The results indicate that M[2]C and M[23]C[6], which are molybdenum-rich carbides, control the embrittling process. This is in agreement with the AES results that embrittlement is caused by the segregation of phosphorus to grain boundaries which, in turn, are controlled by the concentration of molybdenum and chromium in solid solution and/or in carbides. Chromium was found to be segregated at the grain boundaries and it appears to enhance the segregation of phosphorus; whereas molybdenum was not found to be segregated together with phosphorus to grain boundaries.

Item Type: Thesis (Doctoral)
Divisions : Theses
Authors :
NameEmailORCID
Muhammad, Azali bin.
Date : 1982
Contributors :
ContributionNameEmailORCID
http://www.loc.gov/loc.terms/relators/THS
Additional Information : Thesis (Ph.D.)--University of Surrey (United Kingdom), 1982.
Depositing User : EPrints Services
Date Deposited : 22 Jun 2018 14:24
Last Modified : 06 Nov 2018 16:53
URI: http://epubs.surrey.ac.uk/id/eprint/847833

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year


Information about this web site

© The University of Surrey, Guildford, Surrey, GU2 7XH, United Kingdom.
+44 (0)1483 300800