The development of reproducible low dose selenium implantation into GaAs for integrated circuit development.

Leigh, P. A. (1982) The development of reproducible low dose selenium implantation into GaAs for integrated circuit development. Doctoral thesis, University of Surrey (United Kingdom)..

[img]
Preview
Text
10800301.pdf
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (9MB) | Preview

Abstract

The objectives of this work were to study Se implantation into semi-insulating GaAs and achieve reproducible electrical activation with the intention of relating the electrical properties of the implanted layers directly to the requirements of GaAs integrated circuits. The encapsulation of GaAs is essential for high temperature post implant annealing and many problems related to outdiffusion of Ga or As, the redistribution of impurities together with the breakdown of the encapsulant had been reported when this work began in 1977. The implantation results achieved at that time showed a variation in the electrical activation dependent on the type of encapsulant used, the commercial source of the substrates and the species chosen as the implanted impurity. These are reviewed in the literature survey. In this thesis the development of an apparatus for rapid deposition of CVD Si[3]N[4] from mixtures of silane and ammonia is described. The properties of this encapsulant were investigated using a range of physical techniques. Epitaxial n on n[+] GaAs was annealed at high temperatures using the CVD Si[3]N[4] encapsulant to investigate the effects of high temperature annealing on the electrical properties of GaAs. The results of this work established the encapsulant quality to be excellent and suitable for post implant annealing of semi-insulating GaAs. The variations in the quality of semi-insulating substrates were investigated by the electrical measurements of implanted samples and by secondary ion mass on samples implanted with a low dose of Se ions which would be suitable spectrometry analysis. The major part of the implantation studies were for development of integrated circuits. The electrical activation, carrier profile and mobility of a number of samples were determined and the reproducibility of the electrical activation, profile shape and high mobility confirmed. The relationship between the FET dc characteristics and the implanted profile was established both experimentally and by using a computer model.

Item Type: Thesis (Doctoral)
Divisions : Theses
Authors :
NameEmailORCID
Leigh, P. A.
Date : 1982
Contributors :
ContributionNameEmailORCID
http://www.loc.gov/loc.terms/relators/THS
Additional Information : Thesis (Ph.D.)--University of Surrey (United Kingdom), 1982.
Depositing User : EPrints Services
Date Deposited : 22 Jun 2018 13:56
Last Modified : 06 Nov 2018 16:53
URI: http://epubs.surrey.ac.uk/id/eprint/847634

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year


Information about this web site

© The University of Surrey, Guildford, Surrey, GU2 7XH, United Kingdom.
+44 (0)1483 300800